Corrosion and depassivation of a chromia-forming Ni-based alloy in the 0.75Na2O-B2O3-2.75SiO2 melt

V. Szczepan
  • Fonction : Auteur correspondant
C. Petitjean
P.J. Panteix
M. Vilasi

Résumé

Corrosion resistance of nickel based alloys in molten silicates is linked to the temperature. Above a certain temperature, the protection of the alloy by a chromia layer is no more ensured: this depassivation phenomenon leads to active corrosion. Electrochemical methods were used for in situ characterization, and Scanning Electron Microscopy (SEM) and Scanning Electron Transmission Microscopy (STEM) were used in order to measure the oxide thickness after immersion. Corrosion tests with increasing temperature showed that above a certain temperature, the oxide thickness decreased homogeneously leading to the depassivation of the alloy. The different steps of this phenomenon are discussed here.

Domaines

Chimie
Fichier principal
Vignette du fichier
S0010938X19325375.pdf (3.98 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03490161 , version 1 (20-05-2022)

Licence

Paternité - Pas d'utilisation commerciale

Identifiants

Citer

V. Szczepan, C. Petitjean, P.J. Panteix, M. Vilasi. Corrosion and depassivation of a chromia-forming Ni-based alloy in the 0.75Na2O-B2O3-2.75SiO2 melt. Corrosion Science, 2020, 168, pp.108579 -. ⟨10.1016/j.corsci.2020.108579⟩. ⟨hal-03490161⟩
8 Consultations
10 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More