Epitaxial Growth of a Gold Shell on Intermetallic FeRh Nanocrystals

Résumé

In contrast with bimetallics, multimetallic nanoparticle (NPs) can combine different chemical orders in the same NP, which favors an enhanced tuning of their properties. In this work, trimetallic (Fe, Rh, Au) nanocrystals with controlled composition and chemical distribution were grown through a physical vapor deposition route using a two-step process. First FeRh nanocrystals, 8.5 nm of mean diameter, were formed according to a Volmer−Weber growth mode. The growth conditions were tuned so as to achieve the atomic scale chemical order displayed by the intermetallic B2-FeRh phase. Then the gold layer was deposited at a lower temperature. Evidence is given for the complete coverage of the gold shell, which grows epitaxially over the B2-FeRh core exposed facets. These different features are particularly promising for further applications.
Fichier principal
Vignette du fichier
version-accepted.pdf (614.28 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02617536 , version 1 (24-08-2020)

Identifiants

Citer

Patrizio Benzo, Ségolène Combettes, Cécile Garcia, Teresa Hungría, Béatrice Pécassou, et al.. Epitaxial Growth of a Gold Shell on Intermetallic FeRh Nanocrystals. Crystal Growth & Design, 2020, ⟨10.1021/acs.cgd.0c00414⟩. ⟨hal-02617536⟩
87 Consultations
153 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More