Crystallographic effect of a high magnetic field on a solidified hypoeutectic Zn-Al alloy

Abstract : Hypoeutectic Zn-4.45 wt% Al solidified under a high magnetic field was investigated crystallographically. With the field, the primary zinc-rich beta phase is distributed homogeneously and orients with the c axis perpendicular to the magnetic field direction. These results are attributed to the magnetic viscosity resistance force and the magnetocrystalline anisotropy of zinc, respectively. The orientation modification also leads to a preferential alignment of the flat-shaped primary beta dendrites. Furthermore, with the field, the eutectic beta phase shows an orientation character similar to that of the primary beta phase. This arises from its continuous growth with the primary beta phase. In addition, a specific crystallographic orientation relationship (\0001\(beta)parallel to\111\(alpha), < 1 (2) over bar 10 >(beta)parallel to < 110 >(alpha)) exists in some of the eutectics (between the eutectic zinc-rich beta and aluminium-rich alpha phases). However, this orientation relationship is related to the distribution of primary beta dendrites, which originates from the independent nucleation of the pseudo-primary alpha phase attached to the primary beta dendrites.
Type de document :
Article dans une revue
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 2014, 47 (2), pp.606-612. 〈10.1107/S1600576714001939〉
Liste complète des métadonnées

https://hal.univ-lorraine.fr/hal-01503445
Contributeur : Lem3 Ul <>
Soumis le : vendredi 7 avril 2017 - 10:24:08
Dernière modification le : jeudi 11 janvier 2018 - 06:23:43

Lien texte intégral

Identifiants

Collections

Citation

Lei Li, Zongbin Li, Yudong Zhang, Claude Esling, Haitao Liu, et al.. Crystallographic effect of a high magnetic field on a solidified hypoeutectic Zn-Al alloy. JOURNAL OF APPLIED CRYSTALLOGRAPHY, 2014, 47 (2), pp.606-612. 〈10.1107/S1600576714001939〉. 〈hal-01503445〉

Partager

Métriques

Consultations de la notice

96