Texture inheritance from austenite to 7 M martensite in Ni–Mn–Ga melt-spun ribbons

Résumé

In this work, Ni53Mn22Ga25 and Ni51Mn27Ga22 ribbons with austenite and 7 M martensite at room temperature respectively, were prepared by melt-spinning. Through the detailed crystallographic analyses, the preferred orientation in ribbons was confirmed. It is shown that the austenite in Ni53Mn22Ga25 ribbons forms a preferred orientation with {4 0 0}A in parallel to ribbon plane, whereas the 7 M martensite in Ni51Mn27Ga22 ribbons develops the preferred orientation with {2 0 −20}7M, {2 0 20}7M, and {0 4 0}7M crystallographic planes parallel to the ribbon plane. Since {2 0 −20}7M, {2 0 20}7M, and {0 4 0}7M are originated from {4 0 0}A, the preferred orientation in ribbons thus can be inherited after the martensitic transformation. Such texture inheritance is attributed to the intrinsic orientation relationship between austenite and 7 M martensite.

Dates et versions

hal-03080435 , version 1 (17-12-2020)

Identifiants

Citer

Zongbin Li, Yiwen Jiang, Zhenzhuang Li, Yiqiao Yang, Bo Yang, et al.. Texture inheritance from austenite to 7 M martensite in Ni–Mn–Ga melt-spun ribbons. Results in Physics, 2016, 6, pp.428-433. ⟨10.1016/j.rinp.2016.07.012⟩. ⟨hal-03080435⟩
20 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More