Effects of Ni Additions on the High Temperature Expansion, Melting and Oxidation Behaviors of Cobalt-Based Superalloys

Résumé

Nickel is often added to cobalt-based superalloys to stabilize their austenitic structure. In this work the effects of Ni on several high temperature properties of a chromium-rich cobalt-based alloy reinforced by high fraction of TaC carbides are investigated. Different thermal analysis techniques are used: differential scanning calorimetry (DSC), thermo-mechanical analysis (TMA) and thermogravimetry (TG). Results show that the progressive addition of nickel did not induce great modifications of microstructure, refractoriness or thermal expansion. However, minor beneficial effects were noted, including reduction of the melting temperature range and slight decrease in thermal expansion coefficient. The most important improvement induced by Ni addition concerns the hot oxidation behavior. In this way, introducing several tens wt % Ni in this type of cobalt-based alloy may be recommended.
Fichier principal
Vignette du fichier
293 Crystals2021vol11iss2art173.pdf (7.18 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03160194 , version 1 (05-03-2021)

Identifiants

Citer

Patrice Berthod, Lionel Aranda, Jean-Paul Gomis. Effects of Ni Additions on the High Temperature Expansion, Melting and Oxidation Behaviors of Cobalt-Based Superalloys. Crystals, 2021, 11 (2), pp.173. ⟨10.3390/cryst11020173⟩. ⟨hal-03160194⟩
39 Consultations
25 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More