Phase-Transition-Enhanced Thermoelectric Transport in Rickardite Mineral Cu<sub>3– x</sub>Te<sub>2</sub> - Université de Lorraine Accéder directement au contenu
Article Dans Une Revue Chemistry of Materials Année : 2021

Phase-Transition-Enhanced Thermoelectric Transport in Rickardite Mineral Cu3– xTe2

Résumé

The binary copper chalcogenides Cu2−δX (X = S, Se, and Te) have recently gained significant interest due to their high thermoelectric performance at moderate temperatures. In an effort to unveil new Cu-based compounds with promising thermoelectric potential, Cu3– xTe2 rickardite mineral emerged as a candidate based on a purely text mining approach applied by a machine learning method. Polycrystalline samples of Cu3– xTe2 within the homogeneity range (x = 0.1, 0.2) were successfully synthesized from the raw elements by a solid-state method. High-temperature powder X-ray diffraction combined with differential scanning calorimetry and specific heat measurements showed several reversible phase transitions at around 458, 640, and 647 K. Signatures of these transitions were observed on the electronic and thermal transport properties, measured over a broad range of temperatures (5–733 K). The transition undergone by this compound at 647 K results in a crossover from metallic-like to semiconducting-like properties. The combination of high power factor and low thermal conductivity in the high-temperature phase results in improved thermoelectric performances with a peak dimensionless thermoelectric figure-of-merit zT of ∼0.14 at 733 K. The synthetic rickardite mineral is an exciting candidate to be used as a phase change material in broad application areas such as in waste heat harvesting and photovoltaic systems.
Fichier principal
Vignette du fichier
Revised manuscript.pdf (3.21 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03984178 , version 1 (24-03-2023)

Identifiants

Citer

Mujde Yahyaoglu, Melis Ozen, Yurii Prots, Oussama El Hamouli, Vahe Tshitoyan, et al.. Phase-Transition-Enhanced Thermoelectric Transport in Rickardite Mineral Cu3– xTe2. Chemistry of Materials, 2021, 33 (5), pp.1832-1841. ⟨10.1021/acs.chemmater.0c04839⟩. ⟨hal-03984178⟩
41 Consultations
50 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More