Isolation and characterization of lignin from Moroccan sugar cane bagasse: Production of lignin-phenol-formaldehyde wood adhesive - Université de Lorraine Accéder directement au contenu
Article Dans Une Revue Industrial Crops and Products Année : 2013

Isolation and characterization of lignin from Moroccan sugar cane bagasse: Production of lignin-phenol-formaldehyde wood adhesive

Résumé

lignin-based materials were isolated from Moroccan sugar cane bagasse after alkaline delignification. Sugar cane bagasse was subjected to hot water (70 degrees C) and alkaline aqueous solutions (15% of sodium hydroxide (NaOH), 98 degrees C) treatments. The dissolved lignin macromolecules were separated and purified. The isolated solid was then characterized by different complementary analysis (FT-IR; H-1, C-13 NMR; GPC and TGA). In the present work, the possibility of preparing wood adhesives from bagasse lignin has been explored. The results showed that the delignification with 15% NaOH resulted in yields of cellulose and lignin of 42 +/- 2.2% and 13 +/- 1.5%, respectively. The extracted lignin scaffolds exhibits high reactivity due to the high content of hydroxyl group. Their higher molecular weight (2781 g/mol) and good thermal stability (180 degrees C) make them excellent candidates for partial substitution of phenol formaldehyde (PF) resin. A resin formulation in which up to 30% of PP can be substituted by bagasse lignin gave good results and was employed for the elaboration of plywood panels which passed relevant international standard specifications for interior-grade panels.
Fichier non déposé

Dates et versions

hal-01593756 , version 1 (26-09-2017)

Identifiants

Citer

Amine Moubarik, Nabil Grimi, Nadia Boussetta, Antonio Pizzi. Isolation and characterization of lignin from Moroccan sugar cane bagasse: Production of lignin-phenol-formaldehyde wood adhesive. Industrial Crops and Products, 2013, 45, pp.296-302. ⟨10.1016/j.indcrop.2012.12.040⟩. ⟨hal-01593756⟩