Combined synchrotron X-ray diffraction, dilatometry and electrical resistivity in situ study of phase transformations in a Ti2AlNb alloy - Université de Lorraine Accéder directement au contenu
Article Dans Une Revue Materials Characterization Année : 2020

Combined synchrotron X-ray diffraction, dilatometry and electrical resistivity in situ study of phase transformations in a Ti2AlNb alloy

V.A. Esin
M. Dadé
  • Fonction : Auteur
B. Denand
J. Delfosse
  • Fonction : Auteur
P. Sallot
  • Fonction : Auteur

Résumé

Phase transformations in near Ti2AlNb alloy occurring on cooling of 10 °C min−1 from 1020 °C were studied in situ using high energy X-ray diffraction and electrical resistivity measurements coupled with simultaneous dilatometric analysis. From Rietveld refinement of X-ray data, it was established that high temperature range from about 870 to 1020 °C contained partially ordered β phase. The degree of long-range order was of 0.6 at 1020 °C and decreased slowly with temperature decrease and fast when O-phase was formed. The formation of O-Ti2AlNb phase started from about 870 °C and consisted of two stages: (i) fast transformation of partially ordered β into O phase at higher temperatures followed by (ii) slow transformation of fully disordered β into O-phase at lower temperatures. The appearance of O-phase was accompanied by important volume decrease of the alloy as recorded using dilatometry as well as by a decrease of electrical resistivity. The transformations temperatures revealed by high energy X-ray diffraction, dilatometry and electrical resistivity were in good agreement. The obtained results were discussed using thermodynamic simulations carried out with Thermo-Calc software and TCTI2 database.

Domaines

Matériaux
Fichier principal
Vignette du fichier
S1044580320321252.pdf (1.72 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-02955731 , version 1 (26-09-2022)

Licence

Paternité - Pas d'utilisation commerciale

Identifiants

Citer

V.A. Esin, R. Mallick, M. Dadé, B. Denand, J. Delfosse, et al.. Combined synchrotron X-ray diffraction, dilatometry and electrical resistivity in situ study of phase transformations in a Ti2AlNb alloy. Materials Characterization, 2020, 169, pp.110654. ⟨10.1016/j.matchar.2020.110654⟩. ⟨hal-02955731⟩
112 Consultations
39 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More