Grain Refinement and Hardening Induced by Heavy Deformation Using Low Energy High Current Pulsed Electron Beam Surface Treatment

Résumé

The low energy high current pulse electron beam (LEHCPEB) irradiation induces ultra fast dynamic temperature fields in the surface of the material to which is associated dynamic stress fields that causes intense deformation at the material surface and sub-surface. Improved surface properties (hardness, corrosion resistance) can be obtained using the LEHCPEB treatment. Under the “Melting” mode, the top surface (few µm) which is melted and rapidly solidified (107 K/s), can solidify has nano-domains formed from the highly under-cooled melt. The thermal stress wave that propagates in the sub-surface imposes strain hardening and grain size refinement. This induces a sub-surface hardening that can extent over about 100 µm. The use of the “Heating” mode is less conventional. This mode can promote grain size refinement, hardening as well as texture modification without modification of the sample geometry.
Fichier non déposé

Dates et versions

hal-03059587 , version 1 (12-12-2020)

Identifiants

Citer

Thierry Grosdidier, Y. Samih, Nathalie Allain-Bonasso, Bernard Bolle, Z.X. Zou, et al.. Grain Refinement and Hardening Induced by Heavy Deformation Using Low Energy High Current Pulsed Electron Beam Surface Treatment. Materials Science Forum, 2010, 667-669, pp.499-504. ⟨10.4028/www.scientific.net/MSF.667-669.499⟩. ⟨hal-03059587⟩

Collections

CNRS UNIV-LORRAINE
23 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More