Analysis and Testing of Bisphenol A-Free Bio-Based Tannin Epoxy-Acrylic Adhesives

Abstract : A tannin-based epoxy acrylate resin was prepared from glycidyl ether tannin (GET) and acrylic acid. The influence of the reaction condition for producing tannin epoxy acrylate was studied by FT-MIR, C-13-NMR, MALDI-TOF spectroscopy and shear strength. The best reaction conditions for producing tannin epoxy acrylate resin without bisphenol A was by reaction between GET and acrylic acid in the presence of a catalyst and hydroquinone at 95 degrees C for 12 h. FT-MIR, C-13-NMR and MALDI-TOF analysis have confirmed that the resin has been prepared under these conditions. The joints bonded with this resin were tested for block shear strength. The results obtained indicated that the best strength performance was obtained by the bioepoxy-acrylate adhesive resin prepared at 95 degrees C for a 12-h reaction.
Type de document :
Article dans une revue
Polymers, MDPI, 2016, 8 (4), pp.7531-7539. 〈10.3390/polym8040143〉
Liste complète des métadonnées

Littérature citée [16 références]  Voir  Masquer  Télécharger

https://hal.univ-lorraine.fr/hal-01599584
Contributeur : Lermab Ul <>
Soumis le : lundi 2 octobre 2017 - 14:09:27
Dernière modification le : mardi 20 mars 2018 - 10:17:45

Fichier

polymers-08-00143.pdf
Fichiers éditeurs autorisés sur une archive ouverte

Identifiants

Collections

Citation

Shayesteh Jahanshahi, Antonio Pizzi, Ali Abdulkhani, Alireza Shakeri. Analysis and Testing of Bisphenol A-Free Bio-Based Tannin Epoxy-Acrylic Adhesives. Polymers, MDPI, 2016, 8 (4), pp.7531-7539. 〈10.3390/polym8040143〉. 〈hal-01599584〉

Partager

Métriques

Consultations de la notice

54

Téléchargements de fichiers

28