A 3D characterization of equiaxed grains induced by mediated nucleation in additively manufactured Inconel 718 - Université de Lorraine Accéder directement au contenu
Proceedings/Recueil Des Communications IOP Conference Series: Materials Science and Engineering Année : 2023

A 3D characterization of equiaxed grains induced by mediated nucleation in additively manufactured Inconel 718

Julien Zollinger
J Ghanbaja
B Appolaire
  • Fonction : Auteur

Résumé

Abstract In additive manufacturing of Ni-based alloy IN718, what causes Icosahedral Short-Range Order (ISRO) or iQC mediated nucleation of equiaxed grains is still not understood. In order to have a better comprehension of the microstructure formation, a more comprehensive characterization both on grain structure and chemical heterogeneities must be achieved. In this work, a scanning electron microscope equipped with a focused ion beam (FIB) allowed to perform a 3D EDS chemical analysis and EBSD orientation mapping of the volume in an equiaxed grain zone. After the 3D reconstruction of the equiaxed grains has been performed, grain-to-grain orientation analysis allowed to analyze multiple twin boundaries orientation relationships in a volume containing hundreds of grains. Chemical mapping using EDS allowed to identify TiC inclusions from which a five-fold symmetry axis seem to emerge, indicating a potential nucleation site. Such areas were analyzed in transmission electron microscopy (TEM) to investigate the different present phases. The nucleation sequence and potential origin of mediated nucleation are further discussed, opening new prospects for grain refinement in additively manufactured nickel-based alloys.

Dates et versions

hal-04213263 , version 1 (21-09-2023)

Identifiants

Citer

I Cazic, M Engstler, Julien Zollinger, J Ghanbaja, M El Kandaoui, et al.. A 3D characterization of equiaxed grains induced by mediated nucleation in additively manufactured Inconel 718. IOP Conference Series: Materials Science and Engineering, 1274 (1), pp.012002, 2023, ⟨10.1088/1757-899X/1274/1/012002⟩. ⟨hal-04213263⟩
5 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More