Twinning Engineering of a CoCrFeMnNi High-Entropy Alloy - Université de Lorraine Accéder directement au contenu
Article Dans Une Revue Scripta Materialia Année : 2021

Twinning Engineering of a CoCrFeMnNi High-Entropy Alloy

Résumé

Deformation-induced twinning has been a notable example of overcoming the strength/ductility trade-off dilemma as a strengthening mechanism. By borrowing this concept from the area of TWIP steels, we designed a thermomechanical treatment for a CoCrFeMnNi high-entropy alloy to improve its mechanical characteristics. We used pre-straining at 77 K to introduce deformation-induced twins in the microstructure of the alloy, and then recovered it by annealing at 773 K, while avoiding recrystallization. The deformation-induced twins generated by pre-straining at 77 K were retained after this heat treatment, whilst partial recovery of dislocations occurred. As a result, the room-temperature mechanical properties of the alloy, including its strain hardening ability, were improved substantially.
Fichier principal
Vignette du fichier
S1359646221000889.pdf (1.5 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03542064 , version 1 (09-03-2023)

Licence

Paternité - Pas d'utilisation commerciale

Identifiants

Citer

Jongun Moon, Olivier Bouaziz, Hyoung Seop Kim, Yuri Estrin. Twinning Engineering of a CoCrFeMnNi High-Entropy Alloy. Scripta Materialia, 2021, 197, pp.113808. ⟨10.1016/j.scriptamat.2021.113808⟩. ⟨hal-03542064⟩
16 Consultations
40 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More