Twinning Engineering of a CoCrFeMnNi High-Entropy Alloy

Résumé

Deformation-induced twinning has been a notable example of overcoming the strength/ductility trade-off dilemma as a strengthening mechanism. By borrowing this concept from the area of TWIP steels, we designed a thermomechanical treatment for a CoCrFeMnNi high-entropy alloy to improve its mechanical characteristics. We used pre-straining at 77 K to introduce deformation-induced twins in the microstructure of the alloy, and then recovered it by annealing at 773 K, while avoiding recrystallization. The deformation-induced twins generated by pre-straining at 77 K were retained after this heat treatment, whilst partial recovery of dislocations occurred. As a result, the room-temperature mechanical properties of the alloy, including its strain hardening ability, were improved substantially.
Fichier principal
Vignette du fichier
S1359646221000889.pdf (1.5 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03542064 , version 1 (09-03-2023)

Licence

Identifiants

Citer

Jongun Moon, Olivier Bouaziz, Hyoung Seop Kim, Yuri Estrin. Twinning Engineering of a CoCrFeMnNi High-Entropy Alloy. Scripta Materialia, 2021, 197, pp.113808. ⟨10.1016/j.scriptamat.2021.113808⟩. ⟨hal-03542064⟩
18 Consultations
53 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More